Refractory and Polymer Technology MCQs

Welcome to our comprehensive collection of Multiple Choice Questions (MCQs) on Refractory and Polymer Technology, a fundamental topic in the field of Basic Chemical Engineering. Whether you're preparing for competitive exams, honing your problem-solving skills, or simply looking to enhance your abilities in this field, our Refractory and Polymer Technology MCQs are designed to help you grasp the core concepts and excel in solving problems.

In this section, you'll find a wide range of Refractory and Polymer Technology mcq questions that explore various aspects of Refractory and Polymer Technology problems. Each MCQ is crafted to challenge your understanding of Refractory and Polymer Technology principles, enabling you to refine your problem-solving techniques. Whether you're a student aiming to ace Basic Chemical Engineering tests, a job seeker preparing for interviews, or someone simply interested in sharpening their skills, our Refractory and Polymer Technology MCQs are your pathway to success in mastering this essential Basic Chemical Engineering topic.

Note: Each of the following question comes with multiple answer choices. Select the most appropriate option and test your understanding of Refractory and Polymer Technology. You can click on an option to test your knowledge before viewing the solution for a MCQ. Happy learning!

So, are you ready to put your Refractory and Polymer Technology knowledge to the test? Let's get started with our carefully curated MCQs!

Refractory and Polymer Technology MCQs | Page 34 of 52

Discover more Topics under Basic Chemical Engineering

Q331.
Which of the following is generally not drawn into fibre ?

a.

Polyamide

b.

Unsaturated polyesters

c.

Saturated polyesters

d.

Polyacrylonitrile

Discuss
Answer: (b).Unsaturated polyesters
Q332.
Condensation polymerisation of caprolac-tum is carried out in the reactor maintained at a temperature of __________ °C for producing nylon-6.

a.

-20 to 25

b.

50 to 75

c.

100 to 150

d.

250-280

Discuss
Answer: (d).250-280
Q333.
Which of the following is not a natural polymer ?

a.

Nucleic acids e.g. RNA and DNA

b.

Polysaccharides

c.

Polyisoprene

d.

Polyurethane

Discuss
Answer: (d).Polyurethane
Q334.
In case of wet spinning of polymers, the polymer solution is forced through spinnerates into, a coagulating bath to give a filament form. Wet spinning is not used in case of the __________ fibres.

a.

viscose rayon

b.

acrylic

c.

polyvinyl acetate

d.

saturated polyester

Discuss
Answer: (d).saturated polyester
Q335.
Melt spinning of polymers involves the forcing of polymer melt through spinnerettes (fine holes) into an atmosphere kept at a temperature lower than the melting point of the polymer, which causes the fine diameter polymer melt to harden into filaments. Melt spinning is not used in case of the __________ fibres.

a.

acrylic

b.

polyester

c.

nylon 6:6

d.

polypropylene

Discuss
Answer: (a).acrylic
Q336.
Which of the following is not the commercial name of polymethylmethacrylate (PMMA) ?

a.

Perspex

b.

Lucite

c.

Plexiglass

d.

Teflon

Discuss
Answer: (d).Teflon
Q337.
Density of low density polythene is about __________ gm/c.c.

a.

0.38

b.

0.56

c.

0.81

d.

0.91

Discuss
Answer: (d).0.91
Q338.
In step growth polymerisation, condensation occurs in a stepwise manner with or without the elimination of smaller molecules. An example of step growth polymerisation product is

a.

terylene

b.

polybutadiene

c.

PVC

d.

polypropylene

Discuss
Answer: (a).terylene
Q339.
Gutta parcha rubber is

a.

soft & tacky at room temperature.

b.

an isomer of natural rubber.

c.

a thermosetting resin.

d.

recovered by coagulation of rubber latex.

Discuss
Answer: (b).an isomer of natural rubber.
Q340.
The major constituent of laminate of safety glass, which holds the broken glass, pieces in their places during accident (and thus minimises the danger from flying glass fragments) is

a.

polyvinyl alcohol

b.

polyvinyl acetale

c.

polyvinyl butyral

d.

PVC

Discuss
Answer: (c).polyvinyl butyral